1.1 This test method covers determination of the modulus of rupture in bending of specimens cut from graphite electrodes using a simple square cross section beam in four-point loading at room temperature.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM C1025-15(2020) Referenced Document
ASTM C651 Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
ASTM C783 Standard Practice for Core Sampling of Graphite Electrodes
ASTM E4 Standard Practices for Force Verification of Testing Machines
ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
ASTM C1025-15(2020) history
2020ASTM C1025-15(2020) Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite
2015ASTM C1025-15 Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite
1991ASTM C1025-91(2010)e1 Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite
2005ASTM C1025-91(2005) Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite
1991ASTM C1025-91(2000) Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite