SAE AMS4775B-1978
Brazing Filler Metal@ Nickel 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range

Standard No.

SAE AMS4775B-1978

Release Date

1978

Published By

SAE - SAE International

Status

Be replaced 2012-12

Replace By

SAE AMS4775C-1981

Latest

SAE AMS4775L-2023

Scope

Form: This specification covers a nickel alloy in the form of wire@ rod@ strip@ and powder. Application: Primarily for joining corrosion and heat resistant steels and alloys where corrosion and oxidation resistant joints with good strength at elevated temperatures are required. Also may be used as a corrosion and oxidation resistant hard coating.

SAE AMS4775B-1978 history

• 2023 SAE AMS4775L-2023 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus
• 2018 SAE AMS4775K-2018 Nickel Alloy@ Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus (UNS N99600)
• 2010 SAE AMS4775J-2010 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 2005 SAE AMS4775H-2005 Nickel Alloy, Brazing Filler Metal 73Ni 0.75C 4.5Si 14Cr 3.1B 4.5Fe, 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range
• 2000 SAE AMS4775G-2000 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range
• 1995 SAE AMS4775G-1995 Nickel Alloy, Brazing Filler Metal 73Ni 0.75C 4.5Si 14Cr 3.1B 4.5Fe, 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range (Reaffirmed: 01 Aug 2000)
• 1994 SAE AMS4775F-1994 Nickel Alloy@ Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 1992 SAE AMS4775E-1992 Nickel Alloy Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 1988 SAE AMS4775D-1988 Brazing Filler Metal@ Nickel Alloy 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970°F (977° - 1077°C) Solidus-Liquidus Range (UNS N99600)
• 1981 SAE AMS4775C-1981 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970° F (975° to 1075°C) Solidus-Liquidus Range
• 1978 SAE AMS4775B-1978 Brazing Filler Metal@ Nickel 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1956 SAE AMS4775A-1956 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B
• 1952 SAE AMS4775-1952 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - 1C