ASTM C1292-22
Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures

Standard No.

ASTM C1292-22

Release Date

2022

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM C1292-22

Scope

1.1 This test method covers the determination of shear strength of continuous fiber-reinforced ceramic composites (CFCCs) at ambient temperature. The test methods addressed are (1) the compression of a double-notched test specimen to determine interlaminar shear strength, and (2) the Iosipescu test method to determine the shear strength in any one of the material planes of laminated composites. Test specimen fabrication methods, testing modes (load or displacement control), testing rates (load rate or displacement rate), data collection, and reporting procedures are addressed. 1.2 This test method is used for testing advanced ceramic or glass matrix composites with continuous fiber reinforcement having unidirectional (1D) or bidirectional (2D) fiber architecture. This test method does not address composites with 3D fiber architecture or discontinuous fiber-reinforced, whiskerreinforced, or particulate-reinforced ceramics. 1.3 The values stated in SI units are to be regarded as the standard and are in accordance with IEEE/ASTM SI 10. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific hazard statements are given in 8.1 and 8.2. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM C1292-22 Referenced Document

• ASTM C1145 Standard Terminology of Advanced Ceramics
• ASTM D3846 Standard Test Method for In-Plane Shear Strength of Reinforced Plastics
• ASTM D3878 Standard Terminology Composite Materials
• ASTM D5379/D5379M Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method
• ASTM D695 Standard Test Method for Compressive Properties of Rigid Plastics
• ASTM E122 Standard Practice for Calculating Sample Size to Estimate, With a Specified Tolerable Error, the Average for Characteristic of a Lot or Process
• ASTM E177 Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods
• ASTM E337 Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures)
• ASTM E4 Standard Practices for Force Verification of Testing Machines
• ASTM E6 Standard Terminology Relating to Methods of Mechanical Testing
• ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
• IEEE/ASTM SI 10 American National Standard for Metric Practice

ASTM C1292-22 history

• 2022 ASTM C1292-22 Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures
• 2016 ASTM C1292-16 Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures
• 2010 ASTM C1292-10 Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures
• 2000 ASTM C1292-00(2005) Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures
• 2000 ASTM C1292-00 Standard Test Method for Shear Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperatures