SAE AMS5636G-2018
Steel@ Corrosion-Resistant@ Bars and Wire 18Cr - 9.0Ni (302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength (UNS S30200)

Standard No.

SAE AMS5636G-2018

Release Date

2018

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS5636H-2023

Latest

SAE AMS5636H-2023

Scope

Form This specification covers a corrosion-resistant steel in the form of bars and wire 0.75 inch (19 mm) and under in nominal diameter or distance between parallel sides (see 8.4). Application These products have been used typically for small parts@ such as bolts@ screws@ and clevis pins@ requiring corrosion resistance up to 700 ??(371 ?? and which may be fabricated by heading or by machining from bars or wire and roll threading@ but usage is not limited to such applications.

SAE AMS5636G-2018 history

• 2023 SAE AMS5636H-2023 Steel, Corrosion-Resistant, Bars and Wire 18Cr - 9.0Ni (302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength
• 2018 SAE AMS5636G-2018 Steel@ Corrosion-Resistant@ Bars and Wire 18Cr - 9.0Ni (302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength (UNS S30200)
• 2012 SAE AMS5636F-2012 Steel, Corrosion-Resistant, Bars and Wire 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength
• 2011 SAE AMS5636D-2011 STEEL BARS, CORROSION RESISTANT 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated and Cold Drawn 100,000 psi (690 MPa) Tensile Strength
• 2006 SAE AMS5636F-2006 Steel, Corrosion-Resistant, Bars and Wire 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength UNS S30200
• 2000 SAE AMS5636E-2000 Steel, Corrosion Resistant, Bars and Wire 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated and Cold Drawn 100 ksi (689 MPa) Tensile Strength
• 1993 SAE AMS5636E-1993 Steel, Corrosion Resistant, Bars and Wire 18Cr 9.0Ni Solution Heat Treated and Cold Drawn, 100 ksi (689 MPa) Tensile Strength
• 1987 SAE AMS5636D-1987 STEEL BARS@ CORROSION RESISTANT 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated and Cold Drawn 100@000 psi (690 MPa) Tensile Strength (UNS S30200)
• 1981 SAE AMS5636C-1981 STEEL BARS CORROSION RESISTANT 18Cr - 9.0Ni (SAE 30302) Cold Drawn, 100,000 psi (690 MPa) Tensile Strength
• 1971 SAE AMS5636B-1971 STEEL BARS CORROSION RESISTANT 18Cr - 8.5Ni (SAE 30302) Cold Drawn, 100,000 psi (690 MN/m2)
• 1952 SAE AMS5636A-1952 STEEL, CORROSION RESISTANT 18Cr - 8Ni (SAE 30302) Cold Drawn - 100,000 psi
• 1949 SAE AMS5636-1949 STEEL, CORROSION RESISTANT 18Cr - 8Ni (SAE 30302) Cold Drawn - 100,000 psi