SAE AMS4776D-1992
Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)

Standard No.

SAE AMS4776D-1992

Release Date

1992

Published By

SAE - SAE International

Status

Be replaced 2012-12

Replace By

SAE AMS4776E-1994

Latest

SAE AMS4776K-2023

Scope

Form: This specification covers a nickel alloy in the form of wire@ rod@ strip@ foil@ and powder and a viscous mixture (paste) of the powder in a suitable binder. Application: Primarily for joining corrosion and heat resistant steels and alloys requiring corrosion and oxidation resistant joints with good strength at elevated temperatures are required. Also may be used as a corrosion and oxidation resistant hard coating.

SAE AMS4776D-1992 history

• 2023 SAE AMS4776K-2023 Nickel Alloy, Brazing Filler Metal, 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon), 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range
• 2018 SAE AMS4776J-2018 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range (UNS N99610)
• 2010 SAE AMS4776H-2010 Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 2005 SAE AMS4776G-2005 Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range
• 2000 SAE AMS4776F-2000 Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range
• 1995 SAE AMS4776F-1995 Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range (Reaffirmed: 01 Aug 2000)
• 1994 SAE AMS4776E-1994 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1992 SAE AMS4776D-1992 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1988 SAE AMS4776C-1988 Brazing Filler Metal@ Nickel Alloy 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1981 SAE AMS4776B-1981 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1978 SAE AMS4776A-1978 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1956 SAE AMS4776-1956 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - Low Carbon