SAE AMS4764B-1984 PDF

Scope: Form: This specification covers a copper alloy in the form of wire@ rod@ sheet@ strip@ foil@ and powder and a viscous mixture (paste) of the powder in a suitable binder. Application: Primarily for joining corrosion and heat resistant alloys where high strength@ good ductility@ and only short-time oxidation resistance above 1000??(540?? are required. Provides a very good color match for corrosion-resistant steels.

SAE AMS4764B-1984 history

2024 SAE AMS4764H-2024 Copper Alloy, Brazing Filler Metal, 52.5Cu - 38Mn - 9.5Ni, 1615 to 1700 °F (879 to 927 °C) Solidus-Liquidus Range
2019 SAE AMS4764G-2019 Copper Alloy, Brazing Filler Metal 52.5Cu - 38Mn - 9.5Ni 1615 to 1700 °F (879 to 927 °C) Solidus-Liquidus Range
2013 SAE AMS4764F-2013 Copper Alloy, Brazing Filler Metal 52.5Cu - 38Mn - 9.5Ni 1615 to 1700 °F (879 to 927 °C) Solidus-Liquidus Range
2007 SAE AMS4764F-2007 Copper Alloy, Brazing Filler Metal 52.5Cu - 38Mn - 9.5Ni 1615 to 1700 °F (879 to 927 °C) Solidus-Liquidus Range UNS C69950
1999 SAE AMS4764E-1999 Copper Alloy Brazing Filler Metal 52.5Cu 38Mn 9.5Ni, 1615 to 1700°F (879 to 927°C) Solidus-Liquidus Range
1992 SAE AMS4764D-1992 Copper Alloy Brazing Filler Metal 52.5Cu - 38Mn - 9.5Ni 1615 to 1700 Degrees F (879 to 927 Degrees C) Solidus-Liquidus Range (UNS C69950)
1991 SAE AMS4764C-1991 Brazing Filler Metal@ Copper 52.5Cu - 38Mn - 9.5Ni 1615° to 1700°F (879° to 927°C) Solidus-Liquidus Range (UNS C69950)
1984 SAE AMS4764B-1984 BRAZING FILLER METAL@ COPPER 52.5Cu - 38Mn - 9.5Ni 1615° - 1700°F (880° - 925°C) Solidus-Liquidus Range
1978 SAE AMS4764A-1978 BRAZING FILLER METAL@ COPPER 52.5Cu - 38Mn - 9.5Ni 1615° - 1700°F (880° - 925°C) Solidus-Liquidus Range
1966 SAE AMS4764-1966 BRAZING ALLOY Copper Base 39Mn - 9.5Ni