ASTM C874-20 PDF

Scope: 1.1 This test method describes a procedure for comparing the behavior of refractories to the action of molten slag in a rotating test furnace. A reference material should be included in each test and run for comparison. No numeric results are obtained from this test method. Numeric evaluation of test results is the responsibility of the test operator. The test and equipment are patterned after a method developed by Valley Dolomite Corporation.2 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM C874-20 history

2020 ASTM C874-20 Standard Test Method for Rotary Slag Testing of Refractory Materials
2011 ASTM C874-11a Standard Test Method for Rotary Slag Testing of Refractory Materials
2011 ASTM C874-11 Standard Practice for Rotary Slag Testing of Refractory Materials
1999 ASTM C874-99(2009) Standard Practice for Rotary Slag Testing of Refractory Materials
1999 ASTM C874-99(2004) Standard Practice for Rotary Slag Testing of Refractory Materials
1999 ASTM C874-99 Standard Practice for Rotary Slag Testing of Refractory Materials

$Standard Test Method for Rotary Slag Testing of Refractory Materials$