This specification covers a gold-nickel alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, chips, preforms and a viscous mixture (paste) of the powder in a suitable binder.
SAE AMS4787F-2008 history
2022SAE AMS4787H-2022 Gold-Nickel Alloy, Brazing Filler Metal, High Temperature 82Au - 18Ni 1740 °F (949 °C) Solidus-Liquidus Temperature
2017SAE AMS4787G-2017 Gold-Nickel Alloy, Brazing Filler Metal, High Temperature, 82Au 18Ni, 1740°F (949°C) Solidus-Liquidus Temperature
2008SAE AMS4787F-2008 Gold-Nickel Alloy, Brazing Filler Metal, High Temperature 82Au - 18Ni 1740 °F (949 °C) Solidus-Liquidus Temperature
2000SAE AMS4787F-2000 Gold-Nickel Alloy, Brazing Filler Metal, High Temperature, 82Au 18Ni, 1740°F (949°C) Solidus-Liquidus Temperature
1999SAE AMS4787E-1999 Gold-Nickel Alloy@ Brazing Filler Metal@ High Temperature 82Au - 18Ni 1740 Degrees F (949 Degrees C) Solidus-Liquidus Temperature (UNS P00820)
1992SAE AMS4787D-1992 Gold-Nickel Alloy Brazing Filler Metal@ High Temperature 82Au - 18Ni 1740 Degrees F (949 Degrees C) Solidus- Liquidus Temperature
1990SAE AMS4787C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 82Au - 18Ni 1740°F (949°C) Solidus-Liquidus Temperature (UNS P00820)
1984SAE AMS4787B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 82Au - 18Ni@ 1740°F (950°C) Solidus-Liquidus Temperature (UNS P00820)
1978SAE AMS4787A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE 82Au - 18Ni 1740°F (950°C) Solidus-Liquidus Temperature (UNS P00820)
1971SAE AMS4787-1971 BRAZING FILLER METAL@ HIGH TEMPERATURE 82Au - 18Ni