SAE AMS6342A-1946 PDF

Scope: APPLICATION: For parts which require hardenability and physical properties between AMS 6322 and AMS 6415. The hardenability of this steel is approximately the same as that of AMS 6412 but for highly stressed parts the latter@ with its lower carbon and higher nickel contents@ is preferred.

SAE AMS6342A-1946 history

2015 SAE AMS6342K-2015 Steel Bars, Forgings, and Tubing, 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
2011 SAE AMS6342J-2011 Steel Bars, Forgings, and Tubing 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
2001 SAE AMS6342J-2001 Steel Bars, Forgings, and Tubing, 0.80Cr 1.0Ni 0.25Mo (0.38 0.43C)
1994 SAE AMS6342H-1994 STEEL BARS, FORGINGS, AND TUBING 0.8OCr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
1990 SAE AMS6342H-1990 Steel Bars@ Forgings@ and Tubing 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
1985 SAE AMS6342G-1985 STEEL BARS@ FORGINGS@ AND TUBING 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840) (UNS G98400)
1979 SAE AMS6342F-1979 STEEL BARS@ FORGINGS@ AND TUBING 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840) (UNS G98400)
1972 SAE AMS6342E-1972 STEEL BARS@ FORGINGS@ AND TUBING 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
1967 SAE AMS6342D-1967 STEEL BARS@ FORGINGS@ AND TUBING 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
1964 SAE AMS6342C-1964 STEEL BARS@ FORGINGS 0.80Cr - 1.0Ni - 0.25Mo (0.38 - 0.43C) (SAE 9840)
1964 SAE AMS6342-1964 STEEL 1 Ni .8 Cr .25 Mo (.38 - .43 C)
1951 SAE AMS6342B-1951 STEEL BARS AND FORGINGS 1Ni - 0.8Cr - 0.25Mo (0.38-0.43C) (SAE 9840)
1946 SAE AMS6342A-1946 STEEL BARS AND FORGINGS 1Ni-.8Cr-.25Mo (.38-.43C)
1944 SAE AMS6342-1944 STEEL 1 Ni .8 Cr .25 Mo (.38 - .43 C)