SAE AMS4771G-1992
Silver Alloy Brazing Filler Metal 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170 to 1270 Degrees F (632 to 688 Degrees C) Solidus- Liquidus Range

Standard No.

SAE AMS4771G-1992

Release Date

1992

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS4771H-1999

Latest

SAE AMS4771J-2015

SAE AMS4771G-1992 history

• 2015 SAE AMS4771J-2015 Silver Alloy, Brazing Filler Metal 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170 to 1270 °F (632 to 688 °C) Solidus-Liquidus Range
• 2009 SAE AMS4771H-2009 Silver Alloy, Brazing Filler Metal 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170 to 1270 °F (632 to 688 °C) Solidus-Liquidus Range
• 1999 SAE AMS4771H-1999 Silver Alloy, Brazing Filler Metal 50Ag 16Cd 15.5Zn 15.5Cu, 3.0Ni, 1170 to 1270°F (632 to 688°C) Solidus-Liquidus Range
• 1992 SAE AMS4771G-1992 Silver Alloy Brazing Filler Metal 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170 to 1270 Degrees F (632 to 688 Degrees C) Solidus- Liquidus Range
• 1991 SAE AMS4771F-1991 Brazing@ Filler Metal@ Silver 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170° - 1270°F (632° - 688°C) Solidus-Liquidus Range (UNS P07501)
• 1984 SAE AMS4771E-1984 Brazing Filler Metal@ Silver 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170° - 1270°F (630° - 690°C) Solidus-Liquidus Range (UNS P07501)
• 1978 SAE AMS4771D-1978 Brazing Filler Metal@ Silver 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170° - 1270°F (630° - 690°C) Solidus Liquidus Range (UNS P07501)
• 1974 SAE AMS4771C-1974 Brazing Filler Metal@ Silver 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170° - 1270°F (632° - 688°C) Melting Range
• 1972 SAE AMS4771B-1972 Brazing Filler Metal@ Silver 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni 1170 - 1270 F (632 to 688 C) Melting Range
• 1966 SAE AMS4771A-1966 BRAZING ALLOY@ SILVER 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni
• 1958 SAE AMS4771-1958 BRAZING ALLOY@ SILVER 50Ag - 16Cd - 15.5Zn - 15.5Cu - 3.0Ni