ASTM B457-67(2018) PDF

Scope: 1.1 This test method describes the conditions and equipment for measuring the impedance of anodic coatings on aluminum. Such measurements have been used to evaluate the quality of seal of an anodic coating. The test method does not prescribe the procedure for producing the anodic coating, nor the postanodizing treatment usually described as “sealing.” 1.2 This test method is applicable to the rapid, nondestructive testing of anodic coatings. The interpretation of results and correlation of data with service experience and other tests are not within the scope of this test method. 1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM B457-67(2018) history

2018 ASTM B457-67(2018) Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum
1967 ASTM B457-67(2013) Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum
2008 ASTM B457-67(2008)e1 Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum
1998 ASTM B457-67(2003) Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum
1967 ASTM B457-67(1998) Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum