SAE AMS4127K-2019
Aluminum Alloy, Forgings and Rolled or Forged Rings (6061-T6) Solution and Precipitation Heat Treated

Standard No.

SAE AMS4127K-2019

Release Date

2019

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4127L-2024

Latest

SAE AMS4127L-2024

Scope

This specification covers an aluminum alloy in the form of die forgings not over 4 inches (102 mm) in nominal thickness at time of heat treatment , hand forgings with as-forged thickness not exceeding 8 inches (203 mm) and the cross-sectional area not greater than 256 in2, forged or rolled rings 3.5 inches (89 mm) and under in nominal thickness at time of heat treatment and having an OD-to-wall thickness ratio of 10:1 or greater, and stock of any size for forgings and rings (see 8.6).

SAE AMS4127K-2019 history

• 2024 SAE AMS4127L-2024 Aluminum Alloy, Forgings and Rolled or Forged Rings, (6061-T6), Solution and Precipitation Heat Treated
• 2019 SAE AMS4127K-2019 Aluminum Alloy, Forgings and Rolled or Forged Rings (6061-T6) Solution and Precipitation Heat Treated
• 2012 SAE AMS4127J-2012 Aluminum Alloy, Forgings and Rolled or Forged Rings (6061-T6) Solution and Precipitation Heat Treated
• 2005 SAE AMS4127J-2005 Aluminum Alloy, Forgings and Rolled or Forged Rings (6061-T6) Solution and Precipitation Heat Treated UNS A96061
• 1999 SAE AMS4127H-1999 Aluminum Alloy, Forgings and Rolled or Forged Rings, Solution and Precipitation Heat Treated (Reaffirmed: 01 May 1995)
• 1999 SAE AMS4127G-1999 ALUMINUM ALLOY FORGINGS AND ROLLED OR FORGED RINGS 1.0Mg - 0.6Si - 0.2aCu - 0.20Cr (6061-T6) Solution and Precipitation Heat Treated
• 1991 SAE AMS4127G-1991 Aluminum Alloy Forgings and Rolled or Forged Rings 1.0Mg - 0.6Si - 0.28Cu - 0.20Cr (6061- T6) Solution and Precipitation Heat Treated
• 1987 SAE AMS4127F-1987 ALUMINUM ALLOY FORGINGS 1.0 Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T6) Solution and Precipitation Heat Treated (UNS A96061)
• 1982 SAE AMS4127E-1982 ALUMINUM ALLOY FORGINGS 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T6) Solution and Precipitation Heat Treated (UNS A96061)
• 1976 SAE AMS4127D-1976 ALUMINUM ALLOY FORGINGS 1.0Mg - 0.60Si - 0.28Cu - 0.20Cr (6061-T6) (UNS A96061)
• 1966 SAE AMS4127C-1966 ALUMINUM ALLOY FORGINGS 1.0Mg - 0.60Si - 0.30Cu - 0.20Cr (6061-T6)
• 1962 SAE AMS4127B-1962 ALUMINUM ALLOY FORGINGS 1Mg - 0.6Si - 0.3Cu - 0.25Cr (6061-T6)
• 1958 SAE AMS4127A-1958 ALUMINUM ALLOY FORGINGS 1Mg - 0.6Si - 0.3Cu - 0.25Cr (6061-T6)
• 1954 SAE AMS4127-1954 ALUMINUM ALLOY FORGINGS 1Mg - 0.6Si - 0.3Cu - 0.25Cr (61S-T6)