ASTM D6604-00(2022) PDF

Scope: 1.1 This practice covers determination of glass transition temperatures of hydrocarbon (HC) resins by differential scanning calorimetry (DSC). 1.2 This practice is applicable to HC resins as defined in Terminology D6640. The normal operating temperature range is from the cryogenic region to approximately 180 °C. The temperature range can be extended. 1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.4 Further discussion of glass transition can be found in Test Method D3418, and Test Method E1356. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM D6604-00(2022) Referenced Document

ASTM D3418 Standard Test Method for Transition Temperatures of Polymers By Differential Scanning Calorimetry
ASTM D6640 Standard Practice for Collection and Handling of Soils Obtained in Core Barrel Samplers for Environmental Investigations
ASTM E1356 Standard Test Method for Assignment of the Glass Transition Temperatures by Differential Scanning Calorimetry or Differential Thermal Analysis
ASTM E473 Standard Terminology Relating to Thermal Analysis

2022 ASTM D6604-00(2022) Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry
2000 ASTM D6604-00(2017) Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry
2000 ASTM D6604-00(2013) Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry
2000 ASTM D6604-00(2009)e1 Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry
2000 ASTM D6604-00 Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry