SAE AMS4780D-1992
Manganese Alloy Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 Degrees F (965 to 1024 Degrees C) Solidus-Liquidus Range (UNS M26800)

Standard No.

SAE AMS4780D-1992

Release Date

1992

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS4780E-1998

Latest

SAE AMS4780H-2021

SAE AMS4780D-1992 history

• 2021 SAE AMS4780H-2021 Manganese Alloy, Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 °F (966 to 1024 °C) Solidus-Liquidus Range (UNS M26800)
• 2018 SAE AMS4780G-2018 Manganese Alloy@ Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 °F (966 to 1024 °C) Solidus-Liquidus Range (UNS M26800)
• 2012 SAE AMS4780F-2012 Manganese Alloy, Brazing Filler Metal 66Mn 16Ni 16Co 0.80B, 1770 to 1875°F (966 to 1024°C) Solidus-Liquidus Range
• 2007 SAE AMS4780E-2007 Manganese Alloy, Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 °F (966 to 1024 °C) Solidus-Liquidus Range
• 1998 SAE AMS4780E-1998 Manganese Alloy, Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 °F (966 to 1024 °C) Solidus-Liquidus Range UNS M26800
• 1992 SAE AMS4780D-1992 Manganese Alloy Brazing Filler Metal 66Mn - 16Ni - 16Co - 0.80B 1770 to 1875 Degrees F (965 to 1024 Degrees C) Solidus-Liquidus Range (UNS M26800)
• 1991 SAE AMS4780C-1991 Brazing Filler Metal@ Manganese 66Mn - 16Ni - 16Co - 0.80B 1770° - 1875°F (965° - 1025°C) Solidus-Liquidus Range (UNS M26800)
• 1985 SAE AMS4780B-1985 Brazing Filler Metal@ Manganese 66Mn - 16Ni - 16Co - 0.80B 1770° - 1875°F (965° - 1025°C) Solidus-Liquidus Range (UNS M26800)
• 1978 SAE AMS4780A-1978 Brazing Filler Metal@ Manganese 66Mn - 16Ni - 16Co - 0.80B 1770° - 1875°F (965° - 1025°C) Solidus-Liquidus Range (UNS M26800)
• 1962 SAE AMS4780-1962 Brazing Alloy Manganese Base - 16Ni - 16Co - 0.8B