ASTM E159-17 PDF

Scope: 1.1 This test method covers the determination of the mass of hydrogen-reducible constituents in the following metal powders: cobalt, copper, iron, and tungsten. 1.2 This test method is useful for cobalt, copper, and iron powders in the range from 0.05 to 3.0 % oxygen, and for tungsten powder in the range from 0.01 to 0.50 % oxygen. 1.3 This test method does not measure the oxygen contained in oxides such as silicon oxide (SiO2), aluminum oxide (Al2O3), magnesium oxide (MgO), calcium oxide (CaO), titanium dioxide (TiO2), etc. that are not reduced by hydrogen at the test temperatures. 1.4 For total oxygen content, vacuum or inert gas fusion methods are available (see Test Methods E1019). 1.5 The values stated in SI units are to be regarded as the standard. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM E159-17 Referenced Document

ASTM B215 Standard Practices for Sampling Finished Lots of Metal Powders
ASTM B243 Standard Terminology of Powder Metallurgy*， 2023-05-01 Update
ASTM E1019 Standard Test Methods for Determination of Carbon, Sulfur, Nitrogen, and Oxygen in Steel and in Iron, Nickel, and Cobalt Alloys*， 2024-04-21 Update
ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method

2022 ASTM E159-22 Standard Test Method for Loss of Mass in a Reducing Gas Atmosphere for Cobalt, Copper, Tungsten, and Iron Powders (Hydrogen Loss)
2017 ASTM E159-17 Standard Test Method for Loss of Mass in a Reducing Gas Atmosphere for Cobalt, Copper, Tungsten, and Iron Powders (Hydrogen Loss)
2010 ASTM E159-10 Standard Test Method for Loss of Mass in a Reducing Gas Atmosphere for Cobalt, Copper, Tungsten, and Iron Powders (Hydrogen Loss)
2006 ASTM E159-06 Standard Test Method for Loss of Mass in Hydrogen for Cobalt, Copper, Tungsten, and Iron Powders (Hydrogen Loss)
2000 ASTM E159-00 Standard Test Method for Hydrogen Loss of Cobalt, Copper, Tungsten, and Iron Powders