SAE AMS2515-1961
Polytetrafluoroethylene Resin Coating 700 - 750 F Fusion

Standard No.

SAE AMS2515-1961

Release Date

1961

Published By

SAE - SAE International

Status

Be replaced 2010-09

Replace By

SAE AMS2515A-1963

Latest

SAE AMS2515H-2018

Scope

APPLICATION: Primarily for coating metal parts to produce a fused polytetrafluoroethylene resin surface providing dry lubrication@ high heat stability@ and optimum corrosion protection. Applicable primarily to parts which operate at a maximum temperature of 525 F in limited service or 475 F for extended periods. The fusing temperature will result in some softening of cold worked or heat treated aluminum alloys.

SAE AMS2515-1961 history

• 2018 SAE AMS2515H-2018 Polytetrafluoroethylene (PTFE) Resin Coating@ Low Build@ 370 to 400 °C (698 to 752 °F) Fusion
• 2013 SAE AMS2515G-2013 Polytetrafluoroethylene (PTFE) Resin Coating, Low Build, 370 to 400°C (698 to 752°F) Fusion
• 2011 SAE AMS2515F-2011 Polytetrafluoroethylene (PTFE) Resin Coating, Low Build, 370 to 400°C (698 to 752°F) Fusion
• 2003 SAE AMS2515E-2003 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 to 400 °C (698 to 752 °F) Fusion
• 2003 SAE AMS2515D-2003 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 to 400 °C (698 to 752 °F) Fusion
• 1990 SAE AMS2515E-1990 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 - 400 Degrees C (698 - 752 Degrees F) Fusion
• 1983 SAE AMS2515D-1983 Polytetrafluoroethylene Resin Coating Low Build@ 370 Degrees - 400 Degrees C (700 Degrees - 750 Degrees F) Fusion
• 1974 SAE AMS2515C-1974 Polytetrafluoroethylene Resin Coating Low Build@ 700 Degrees - 750 Degrees F (371 Degrees - 399 Degrees C) Fusion
• 1965 SAE AMS2515B-1965 Polytetrafluoroethylene Resin Coating Low Build@ 700 - 750 F (371 - 399 C) Fusion
• 1963 SAE AMS2515A-1963 Polytetrafluoroethylene Resin Coating Low Build@ 700 - 750 F (370 - 400 C) Fusion
• 1961 SAE AMS2515-1961 Polytetrafluoroethylene Resin Coating 700 - 750 F Fusion