Full Description 1.1 This test method covers the determination of length change of mortar bars immersed in a sulfate solution. Mortar bars made using mortar described in Test Method C109/C109M are cured until they attain a compressive strength of 20.0 MPa ± 1.0 MPa [3000 psi ± 150 psi], as measured using cubes made of the same mortar, before the bars are immersed. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the inch-pound units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM C1012/C1012M-24 history
2024ASTM C1012/C1012M-24 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2018ASTM C1012/C1012M-18b Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2018ASTM C1012/C1012M-18a Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2018ASTM C1012/C1012M-18 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2015ASTM C1012/C1012M-15 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2013ASTM C1012/C1012M-13 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2012ASTM C1012/C1012M-12 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2010ASTM C1012/C1012M-10 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2009ASTM C1012/C1012M-09 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2004ASTM C1012-04 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2003ASTM C1012-03 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
2002ASTM C1012-02 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
1995ASTM C1012-95a Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
1995ASTM C1012-95 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution