SAE AMS6361A-1972
STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125@000 psi (862 MPa) Tensile Strength

Standard No.

SAE AMS6361A-1972

Release Date

1972

Published By

SAE - SAE International

Status

Be replaced 2012-12

Replace By

SAE AMS6361B-1984

Latest

SAE AMS6361G-2018

Scope

Form: This specification covers an aircraft-quality@ low-alloy steel in the form of round@ seamless tubing having a wall thickness not greater than 0.188 inch (4.78 mm). Application: This tubing has been typically used in thin-walled sections where a minimum tensile strength of 125 ksi (862 MPa) is required.

SAE AMS6361A-1972 history

• 2018 SAE AMS6361G-2018 Steel Tubing@ Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125 ksi (862 MPa) Tensile Strength (UNS G41300)
• 2014 SAE AMS6361F-2014 Steel Tubing, Seamless, 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125 ksi (862 MPa) Tensile Strength
• 2009 SAE AMS6361E-2009 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125 ksi (862 MPa) Tensile Strength
• 2005 SAE AMS6361E-2005 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125 ksi (862 MPa) Tensile Strength UNS G41300
• 2000 SAE AMS6361D-2000 Steel Tubing, Seamless 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125 ksi (862 MPa) Tensile Strength UNS G41300
• 1994 SAE AMS6361C-1994 STEEL TUBING, SEAMLESS ROUND 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125,000 psi (862 MPa) Tensile Strength
• 1990 SAE AMS6361C-1990 Steel Tubing@ Seamless Round 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125@000 psi (862 MPa) Tensile Strength
• 1984 SAE AMS6361B-1984 STEEL TUBING@ SEAMLESS ROUND 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125@000 psi (860 MPa) Tensile Strength (UNS G41300)
• 1972 SAE AMS6361A-1972 STEEL TUBING@ SEAMLESS 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) 125@000 psi (862 MPa) Tensile Strength
• 1942 SAE AMS6361-1942 STEEL TUBING@ (SEAMLESS)@ ROUND Chromium Molybdenum (.27 - .33Carbon) (125@000 T.S. - .188 Max Wall Thickness)