ASTM E103-17 PDF

Scope: 1.1 This practice covers a procedure for rapid indentation hardness testing of metallic materials. 1.2 This practice includes additional requirements in Annex A1 for the direct, indirect, and daily verification of rapid indentation hardness testing machines. 1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM E103-17 Referenced Document

ASTM E10 Standard Test Method for Brinell Hardness of Metallic Materials*， 2023-08-03 Update
ASTM E74 Standard Practices for Calibration and Verification for Force-Measuring Instruments*， 2018-02-01 Update
ISO/IEC 17011 Conformity assessment — Requirements for accreditation bodies accrediting conformity assessment bodies*， 2024-04-20 Update
ISO/IEC 17025 General requirements for the competence of testing and calibration laboratories [Standard in French]*， 2017-11-01 Update

2017 ASTM E103-17 Standard Practice for Rapid Indentation Hardness Testing of Metallic Materials
2012 ASTM E103-12 Standard Practice for Rapid Indentation Hardness Testing of Metallic Materials
1984 ASTM E103-84(2002) Standard Test Method for Rapid Indentation Hardness Testing of Metallic Materials
1996 ASTM E103-84(1996)e1 Standard Test Method for Rapid Indentation Hardness Testing of Metallic Materials
1984 ASTM E103-84(1996) Standard Test Method for Rapid Indentation Hardness Testing of Metallic Materials