ASTM B947-14(2020)e1
Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate

Standard No.

ASTM B947-14(2020)e1

Release Date

2014

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM B947-14(2020)e1

Scope

1.1 This practice establishes the controls required for hot rolling mill solution heat treatment of the 6xxx series aluminum alloy plate in Table 1 when ASTM material specifications allow use of this process instead of furnace solution heat treatment. For the alloys listed in Table 1, this practice is an alternate process to solution heat treatment in a furnace, such as specified in Practice B918/B918M as the preliminary step for the attainment of T651-type tempers (see ANSI H35.1/ H35.1M). 1.2 This practice applies only to hot rolling mill solution heat treatment of plate for the listed aluminum alloys. Precipitation hardening (aging), processing, and equipment calibration for aging shall meet the practice and requirements of Practice B918/B918M. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM B947-14(2020)e1 Referenced Document

• ASTM B209 Standard Specification for Aluminum and Aluminum- Alloy Sheet and Plate
• ASTM B209M Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate (Metric)*， 2024-04-20 Update
• ASTM B557 Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
• ASTM B557M Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products [Metric]
• ASTM B881 Standard Terminology Relating to Aluminum- and Magnesium- Alloy Products
• ASTM B918/B918M Standard Practice for Heat Treatment of Wrought Aluminum Alloys*， 2020-12-01 Update
• ASTM E2281 Standard Practice for Process Capability and Performance Measurement*， 2020-10-01 Update

ASTM B947-14(2020)e1 history

• 2014 ASTM B947-14(2020)e1 Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate
• 2014 ASTM B947-14 Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate
• 2006 ASTM B947-06(2013) Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate
• 2006 ASTM B947-06 Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate